Kohimo Co. was able to reduce production time and improve weld quality in the production of spheres using Gullco products and technologies. In this project Kohimo was manufacturing 18m. Diameter spheres from 20mm. Thick steel in Estonia.
The method used in order to reduce production cost was single side welding, 60 deg. Incl angle 4-5mm gap 2 mm root-face using 1.2 mm flux cored wire.
Gullco Flex Kat Oscillator Combination units running on flexible Kat Flex Track were used to perform the weld operation.
This Gullco equipment combines welding gun oscillation movement with precise travel speed to produce a wide variety of angular and step weld patterns.
The integrated control system directs both the Flex Carriage travel speed/direction and the weld gun movement/ operation.
This enables pre-setting of stroke speed, oscillation and carriage dwell times carriage delay/ start wire feed start. When combined with the precision controlled travel speed of the Kat carriage, a wide range of weld patterns can be produced.
Gullco KATBAK Ceramic Weld Backings enable X-ray quality root welds in one pass, full penetration welding from one side and uniform backbeads of finish quality. I
nside the sphere, strong backs were used with cut-outs in them...allowing KATBAK ceramics to be applied through. These strong backs maintained the shape of the sphere so that 100% weld penetration could be maintained.
Two Gullco Flex Kat Oscillator Combination units were mounted on a single flexible track working into the middle of the same joint. This, combined with the placement of Gullco 1G93-R Katbak ceramics on the inside of the vessel increased the quality and improved efficiency of the weld. This process resulted in the root side of the joint being as good as the outside with no defects and very few stops and starts in the joint.